- 密度 [g/cm3]: 1.45
- 拉伸強度 [MPa]: 100.0
- 彎曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in3 | ISO R 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ISO-DIS 527 |
| Tensile Modulus | 8.00 GPa | 1160 ksi | DIN 53457 |
| Flexural Strength | 180 MPa | 26100 psi | DIN 54352 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | DIN 53457 |
| Compressive Strength | 320 MPa | 46400 psi | ISO 604 |
| Izod Impact Resistance | 5.50 J/cm2 | 26.2 ft-lb/in2 | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Coefficient of Friction, Dynamic | 0.20 | 0.20 | no lube; Steel 2162, Rvst=2E-6m, p=0.05 Mpa, v=0.6 m/s, t=40°C |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous |