- 密度 [g/cm3]: 1.52
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.27
- 斷裂伸長率 [%]: 80.0
- 彎曲強度 [MPa]: 45.0
- 彎曲模量 [MPa]: 4.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in3 | ASTM D792 |
| Apparent Bulk Density | 0.550 g/cc | 0.0199 lb/in3 | ASTM D1895 |
| Water Absorption | 0.30 % | 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | Compression; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ASTM D638 |
| Flexural Yield Strength | 80.0 MPa | 11600 psi | ASTM D790 |
| Flexural Modulus | 4.80 GPa | 696 ksi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 8.90 kV/mm | 226 kV/in | ASTM D149 |
| Comparative Tracking Index | 180 V | 180 V | UL 746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 174 °C | 345 °F | ASTM D648 |
| UL RTI, Electrical | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical with Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| UL RTI, Mechanical without Impact | 150 °C @Thickness 1.57 mm | 302 °F @Thickness 0.0618 in | |
| Flammability, UL94 | V-1 @Thickness 6.35 mm | V-1 @Thickness 0.250 in | |
| V-1 @Thickness 6.35 mm | V-1 @Thickness 0.250 in | ||