- 密度 [g/cm3]: 0.04
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.0400 g/cc | 0.00145 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Compressive Yield Strength | >= 0.621 MPa | >= 90.0 psi | Bare, min |
| >= 0.724 MPa | >= 105 psi | Stabilized, min | |
| 0.827 MPa | 120 psi | Bare, typ | |
| 0.965 MPa | 140 psi | Stabilized, typ | |
| Shear Modulus | 0.0207 GPa | 3.00 ksi | Plate Shear, W Direction, typ |
| 0.496 GPa | 72.0 ksi | Plate Shear, L Direction, typ | |
| Shear Strength | >= 0.276 MPa | >= 40.0 psi | Plate Shear, W Direction, min |
| 0.310 MPa | 45.0 psi | Plate Shear, W Direction, typ | |
| >= 0.496 MPa | >= 72.0 psi | Plate Shear, L Direction, min | |
| 0.586 MPa | 85.0 psi | Plate Shear, L Direction, typ | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 177 °C | 350 °F | |