- 密度 [g/cm3]: 1.4
- 吸水率 [%]: 0.8
- 缺口沖擊強度: 6.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1 |
| Water Absorption | 0.80 % | 0.80 % | 24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 90.0 MPa @Thickness >=1.50 mm | 13100 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
| Modulus of Elasticity | 8.00 GPa @Thickness >=1.50 mm | 1160 ksi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
| Flexural Strength | 140 MPa @Thickness >=1.50 mm | 20300 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 |
| Compressive Strength | 280 MPa @Thickness >=5.00 mm | 40600 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
| Shear Strength | 50.0 MPa @Thickness >=5.00 mm | 7250 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Thickness >=5.00 mm | 2.86 ft-lb/in2 @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 1.00e+6 ohm @Thickness >=3.00 mm | 1.00e+6 ohm @Thickness >=0.118 in | 24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
| Dielectric Strength | 0.600 kV/mm @Thickness >=3.00 mm | 15.2 kV/in @Thickness >=0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2 |
| 2.00 kV/mm @Thickness 3.00 mm | 50.8 kV/in @Thickness 0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1 | |
| Comparative Tracking Index | 100 V @Thickness 3.00 mm | 100 V @Thickness 0.118 in | IEC 60112; IEC/EN 60893-2 6.4 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Inert | 100 °C @Thickness 0.000 mm, Time 7.20e+7 sec | 212 °F @Thickness 0.000 in, Time 20000 hour | IEC 60216; IEC/EN 60893-2 7.1 |