- 密度 [g/cm3]: 1.95
- 吸水率 [%]: 0.53
- 缺口沖擊強(qiáng)度: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.95 g/cc | 0.0704 lb/in3 | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1 |
| Water Absorption | 0.53 % | 0.53 % | 24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 250 MPa @Thickness >=1.50 mm | 36300 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
| Modulus of Elasticity | 19.0 GPa @Thickness >=1.50 mm | 2760 ksi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
| Flexural Strength | 120 MPa @Thickness >=250 mm | 17400 psi @Thickness >=9.84 in | ISO 178; IEC/EN 60893-2 5.1 |
| 160 MPa @Thickness >=200 mm | 23200 psi @Thickness >=7.87 in | ISO 178; IEC/EN 60893-2 5.1 | |
| 210 MPa @Thickness >=150 mm | 30500 psi @Thickness >=5.91 in | ISO 178; IEC/EN 60893-2 5.1 | |
| 330 MPa @Thickness >=50.0 mm | 47900 psi @Thickness >=1.97 in | ISO 178; IEC/EN 60893-2 5.1 | |
| 350 MPa @Thickness >=1.50 mm | 50800 psi @Thickness >=0.0591 in | 24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 | |
| 350 MPa @Thickness >=20.0 mm | 50800 psi @Thickness >=0.787 in | ISO 178; IEC/EN 60893-2 5.1 | |
| 370 MPa @Thickness >=100 mm | 53700 psi @Thickness >=3.94 in | ISO 178; IEC/EN 60893-2 5.1 | |
| Compressive Strength | 500 MPa @Thickness >=5.00 mm | 72500 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
| 400 MPa @Treatment Temp. 250 °C, Time 3600 sec | 58000 psi @Treatment Temp. 482 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 430 MPa @Treatment Temp. 200 °C, Time 3600 sec | 62400 psi @Treatment Temp. 392 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 470 MPa @Treatment Temp. 150 °C, Time 3600 sec | 68200 psi @Treatment Temp. 302 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 530 MPa @Treatment Temp. 100 °C, Time 3600 sec | 76900 psi @Treatment Temp. 212 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 620 MPa @Treatment Temp. 50.0 °C, Time 3600 sec | 89900 psi @Treatment Temp. 122 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| 660 MPa @Treatment Temp. 20.0 °C, Time 3600 sec | 95700 psi @Treatment Temp. 68.0 °F, Time 1.00 hour | ISO 604; IEC/EN 60893-2 5.3 | |
| Shear Strength | 50.0 MPa @Thickness >=5.00 mm | 7250 psi @Thickness >=0.197 in | 24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
| Izod Impact, Notched (ISO) | 55.0 kJ/m2 @Thickness >=5.00 mm | 26.2 ft-lb/in2 @Thickness >=0.197 in | 24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3 |
| Electrical Properties | Metric | English | Comments |
| Insulation Resistance | 1.00e+9 ohm @Thickness >=3.00 mm | 1.00e+9 ohm @Thickness >=0.118 in | 24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
| Dielectric Constant | 5.0 @Thickness <=3.00 mm, Frequency 50.0 Hz | 5.0 @Thickness <=0.118 in, Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| Dielectric Strength | 1.20 kV/mm @Thickness >=3.00 mm | 30.5 kV/in @Thickness >=0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2 |
| 10.0 kV/mm @Thickness 3.00 mm | 254 kV/in @Thickness 0.118 in | 24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1 | |
| Dissipation Factor | 0.030 @Frequency 50.0 Hz | 0.030 @Frequency 50.0 Hz | 96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| Comparative Tracking Index | 100 V @Thickness 3.00 mm | 100 V @Thickness 0.118 in | IEC 60112; IEC/EN 60893-2 6.4 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Inert | 155 °C @Thickness 0.000 mm, Time 7.20e+7 sec | 311 °F @Thickness 0.000 in, Time 20000 hour | IEC 60216; IEC/EN 60893-2 7.1 |
| Flammability, UL94 | V-0 | V-0 | IEC/EN 60893-2 7.2; IEC 60695-11-10 |