- 密度 [g/cm3]: 1.47
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.29
- 斷裂伸長率 [%]: 76.0
- 彎曲強度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0060 cm/cm | 0.0060 in/in | Compression; ASTM D955 |
| 0.0080 cm/cm | 0.0080 in/in | Injection; ASTM D955 | |
| 0.0080 cm/cm | 0.0080 in/in | Transfer; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D651 |
| Flexural Yield Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Compressive Yield Strength | 217 MPa | 31500 psi | ASTM D695 |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.350 J/cm2 | 1.67 ft-lb/in2 | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | ASTM D257 |
| Insulation Resistance | 1.00e+9 ohm | 1.00e+9 ohm | After Boiling; ASTM D257 |
| 1.00e+11 ohm | 1.00e+11 ohm | Normal; ASTM D257 | |
| Dielectric Strength | 13.8 kV/mm | 351 kV/in | ASTM D149 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Comparative Tracking Index | 175 - 250 V | 175 - 250 V | UL PLC 3 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Two Hour Heat Resistance per ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.620 mm | V-0 @Thickness 0.0244 in | |