- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.4
- 缺口沖擊強度: 0.29
- 斷裂伸長率 [%]: 88.0
- 彎曲強度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | Compression; ASTM D955 |
| 0.0090 cm/cm | 0.0090 in/in | Transfer; ASTM D955 | |
| 0.012 cm/cm | 0.012 in/in | Injection; ASTM D955 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.0 MPa | 7980 psi | ASTM D651 |
| Flexural Yield Strength | 88.0 MPa | 12800 psi | ASTM D790 |
| Compressive Yield Strength | 207 MPa | 30000 psi | ASTM D695 |
| Izod Impact, Notched | 0.290 J/cm | 0.543 ft-lb/in | ASTM D256 |
| Charpy Impact, Notched | 0.320 J/cm2 | 1.52 ft-lb/in2 | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Insulation Resistance | 1.00e+8 ohm | 1.00e+8 ohm | After Boiling; ASTM D257 |
| 1.00e+10 ohm | 1.00e+10 ohm | Normal; ASTM D257 | |
| Dielectric Strength | 9.10 kV/mm | 231 kV/in | ASTM D149 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL PLC 4 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Two Hour Heat Resistance per ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.790 mm | HB @Thickness 0.0311 in | |