- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 0.22
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 - 1.37 g/cc | 0.0477 - 0.0495 lb/in3 | Molding; IS 867-1963 |
| Apparent Bulk Density | 0.600 - 0.680 g/cc | 0.0217 - 0.0246 lb/in3 | IS 867-1963 |
| Water Absorption | 0.20 - 0.40 % | 0.20 - 0.40 % | IS 13411-1993 |
| Linear Mold Shrinkage | 0.0075 - 0.0090 cm/cm | 0.0075 - 0.0090 in/in | IS 13411-1992 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.0 - 55.0 MPa | 6670 - 7980 psi | 5 mm/min.; IS 867-1963 |
| Shear Strength | 66.0 - 75.0 MPa | 9570 - 10900 psi | 2mm/min.; IS 867-1963 |
| Izod Impact, Notched | 0.220 - 0.300 J/cm | 0.412 - 0.562 ft-lb/in | IS 13411-1992 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+11 - 3.16e+11 ohm-cm | 1.00e+11 - 3.16e+11 ohm-cm | IS 3396-1979 |
| Surface Resistance | 1.00e+10 - 3.16e+10 ohm | 1.00e+10 - 3.16e+10 ohm | IS 3396-1979 |
| Dielectric Strength | 5.00 - 7.00 kV/mm @Temperature 90.0 °C | 127 - 178 kV/in @Temperature 194 °F | IS 2584-1963 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 65.0 - 85.0 °C | 149 - 185 °F | |
| Front Barrel Temperature | 85.0 - 95.0 °C | 185 - 203 °F | |
| Nozzle Temperature | <= 105 °C | <= 221 °F | |
| Mold Temperature | 160 - 180 °C | 320 - 356 °F | |
| Injection Pressure | 98.0 - 196 MPa | 14200 - 28400 psi | |
| Hold Pressure | 58.8 MPa | 8530 psi | |
| Cure Time | 0.200 - 0.333 min | 0.00333 - 0.00556 hour | per mm |
| Shelf Life | 1.50 Month | 1.50 Month | 27-30°C |
| 4.00 Month | 4.00 Month | below 20°C | |