- 斷裂伸長率 [%]: 135
- 彎曲強度 [MPa]: 105.0
- 彎曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Viscosity | 3.00e+6 cP | 3.00e+6 cP | target viscosity before cure |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Barcol | 71 | 71 | Bottom of sample; cure light intensity of 660 mWatts/cm2. C2 shade. |
| 85 | 85 | Top of sample; cure light intensity of 660 mWatts/cm2. C2 shade. | |
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | Diametral tensile strength |
| Flexural Yield Strength | 135 MPa | 19600 psi | |
| Flexural Modulus | 14.5 GPa | 2100 ksi | |
| Compressive Yield Strength | 470 MPa | 68200 psi | |
| Adhesive Bond Strength | 28.0 MPa | 4060 psi | Bond strength to dentin using a dental adhesive system; C2 color |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 °C | 68.0 °F | Light cured |