- 密度 [g/cm3]: 1.273
- 拉伸強度 [MPa]: 13.9
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.273 g/cc | 0.04599 lb/in3 | ASTM D3165 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 64 | 64 | ASTM D2240 | ||
| 53.76 @Treatment Temp. 125 °C, Time 252000 sec | 53.76 @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Tensile Strength, Yield | 13.9 MPa | 2020 psi | ASTM D412 | ||
| 8.40 MPa @Treatment Temp. 125 °C, Time 252000 sec | 1220 psi @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Elongation at Break | 602 % | 602 % | ASTM D412 | ||
| 375.65 % @Treatment Temp. 125 °C, Time 252000 sec | 375.65 % @Treatment Temp. 257 °F, Time 70.0 hour | Heat Aging; ASTM D573 | |||
| Compressive Modulus | 0.000710 GPa @Strain 5.00 % | 0.103 ksi @Strain 5.00 % | |||
| 0.00126 GPa @Strain 10.0 % | 0.183 ksi @Strain 10.0 % | ||||
| 0.00183 GPa @Strain 20.0 % | 0.265 ksi @Strain 20.0 % | ||||
| 0.00238 GPa @Strain 25.0 % | 0.345 ksi @Strain 25.0 % | ||||
| Compression Set | 6.5 % @Temperature 100 °C, Time 252000 sec | 6.5 % @Temperature 212 °F, Time 70.0 hour | ASTM D395 | ||
| Descriptive Properties | |||||
| Color | Green | ||||