- 密度 [g/cm3]: 1.22
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Carrier; Arlon SQA-TMS-003 | ||
| 381 microns | 15.0 mil | Rubber; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 69 | 69 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 10.0 MPa | 1450 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 654 % | 654 % | Silicone Property; ASTM D412 | ||
| Shear Strength | 5.72 MPa | 829 psi | ASTM D1002 | ||
| Tear Strength | 49.1 kN/m | 280 pli | Die B; Silicone Property; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 49.80 kV/mm | 1265 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Total Product Weight (oz/yd2) | 18.1 | Arlon SQA-TMS-025 | |||