- 密度 [g/cm3]: 1.24
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 305 microns | 12.0 mil | Side 1; Arlon SQA-TMS-003 | ||
| 406 microns | 16.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 711 microns | 28.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 44 | 44 | Silicone Property; Arlon SQA-TMS-014 | ||
| Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; Arlon SQA-TMS-008 | ||
| Elongation at Break | 650 % | 650 % | Silicone Property; Arlon SQA-TMS-008 | ||
| Tear Strength | 14.5 kN/m | 83.0 pli | Die B; Silicone Property; Arlon SQA-TMS-029 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | Arlon SQA-TMS-020 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 220 °C | 428 °F | E54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| Shelf Life | 60.0 Month @Temperature 21.1 °C | 60.0 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Green | ||||
| Total Product Weight (oz/yd2) | 28.1 | Arlon SQA-TMS-025 | |||