- 密度 [g/cm3]: 1.26
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 102 microns | 4.00 mil | Layer 1; Arlon SQA-TMS-003 | ||
| 178 microns | 7.00 mil | Layer 2; Arlon SQA-TMS-003 | |||
| 457 microns | 18.0 mil | Substrate | |||
| 737 microns | 29.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 59 | 59 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.93 MPa | 1150 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 350 % | 350 % | Silicone Property; ASTM D412 | ||
| Tear Strength | 16.7 kN/m | 95.0 pli | Silicone Property; ASTM D6242 | ||
| Peel Strength | 2.77 kN/m | 15.8 pli | Bond Strength; ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 14.6 kV/mm | 370 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | HB | HB | at 220°C per card E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 31.5 | Arlon SQA-TMS-025 | |||