- 密度 [g/cm3]: 1.35
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Layer 1; Arlon SQA-TMS-003 | ||
| 191 microns | 7.50 mil | Layer 2; Arlon SQA-TMS-003 | |||
| 483 microns | 19.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 749 microns | 29.5 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 4.83 MPa | 700 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 200 % | 200 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.31 kN/m | 7.50 pli | Bond Strength (S1 to S1); ASTM D624 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | 13.8 kV/mm | 350 kV/in | ASTM D149 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| UL RTI, Electrical | 200 °C | 392 °F | File E54153 | ||
| UL RTI, Mechanical without Impact | 200 °C | 392 °F | File E54153 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 121 °C | 0.250 hour @Pressure 50.0 psi, Temperature 250 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 23.9 °C | 6.00 Month @Temperature 75.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 27.8 | Arlon SQA-TMS-025 | |||