| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 127 microns | 5.00 mil | Substrate | ||
| 1020 microns | 40.0 mil | Rubber | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 55 | 55 | Silicone Property | ||
| Tensile Strength | 6.21 - 7.58 MPa | 900 - 1100 psi | Silicone Property | ||
| Elongation at Break | 450 - 550 % | 450 - 550 % | Silicone Property | ||
| Tear Strength | >= 35.1 kN/m | >= 200 pli | Silicone Property | ||
| Compression Set | <= 28 % | <= 28 % | After Post-cure; Silicone Property | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 177 °C | 0.500 hour @Temperature 350 °F | Recommended Cure Cycle | ||
| 240 min @Temperature 204 °C | 4.00 hour @Temperature 400 °F | Recommended Post Cure Cycle - After 30 minute ramp up cycle | |||
| Shelf Life | 3.00 Month @Temperature 4.44 °C | 3.00 Month @Temperature 40.0 °F | |||
| Descriptive Properties | |||||
| Color | Clear | Kodacel | |||
| Red | Silicone | ||||
| Total Product Weight (oz/yd2) | 69 | ||||