| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Thickness | 102 microns | 4.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 178 microns | 7.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Substrate; Arlon SQA-TMS-003 | |||
| 635 microns | 25.0 mil | Overall Thickness; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 60 | 60 | Silicone Property | ||
| Tensile Strength | 6.89 MPa | 1000 psi | Silicone Property | ||
| Elongation at Break | 375 % | 375 % | Silicone Property | ||
| Peel Strength | >= 1.05 kN/m | >= 6.00 pli | Bond Strength | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Strength | >= 15.7 kV/mm | >= 400 kV/in | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Inert | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Flammability, UL94 | HB | HB | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended post Cure Cycle | ||
| 15.0 min @Pressure 0.345 MPa, Temperature 177 °C | 0.250 hour @Pressure 50.0 psi, Temperature 350 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 °C | 6.00 Month @Temperature 70.0 °F | |||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 27.1 | ||||
| Uncoated Fabric Break Strength (lb/in) | 300 | Fill Direction; Substrate Property | |||
| 450 | Warp Direction; Substrate Property | ||||