- 密度 [g/cm3]: 1.4
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 76.2 microns | 3.00 mil | Side 1; Arlon SQA-TMS-003 | ||
| 76.2 microns | 3.00 mil | Side 2; Arlon SQA-TMS-003 | |||
| 76.2 microns | 3.00 mil | Liner 1 | |||
| 76.2 microns | 3.00 mil | Liner 2 | |||
| 203 microns | 8.00 mil | Substrate; Arlon SQA-TMS-003 | |||
| 356 microns | 14.0 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 58 | 58 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 7.58 MPa | 1100 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 250 % | 250 % | Silicone Property; ASTM D412 | ||
| Peel Strength | 1.26 kN/m | 7.20 pli | Bond Strength; ASTM D624 | ||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 232 °C | 450 °F | |||
| Minimum Service Temperature, Air | -56.7 °C | -70.0 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 120 min @Temperature 204 °C | 2.00 hour @Temperature 400 °F | Recommended Postcure Cycle | ||
| 15.0 min @Pressure 0.0689 - 0.345 MPa, Temperature 149 °C | 0.250 hour @Pressure 10.0 - 50.0 psi, Temperature 300 °F | Recommended Cure Cycle | |||
| Shelf Life | 6.00 Month @Temperature 21.1 - 26.7 °C | 6.00 Month @Temperature 70.0 - 80.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Red | ||||
| Total Product Weight (oz/yd2) | 15 | Arlon SQA-TMS-025 | |||
| Uncoated Fabric Break Strength | 200 | Fill Strength, Substrate Property, Arlon SQA-TMS-026 | |||
| 250 | Warp Strength, Substrate Property, Arlon SQA-TMS-026 | ||||