- 密度 [g/cm3]: 2.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 2.60 g/cc | 0.0939 lb/in3 | Silicone Property; Arlon SQA-TMS-024 | ||
| Thickness | 25.4 microns | 1.00 mil | Liner | ||
| 76.2 microns | 3.00 mil | Carrier | |||
| 203 microns | 8.00 mil | Overall; Arlon SQA-TMS-003 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 57 | 57 | Silicone Property; ASTM D2240 | ||
| Tensile Strength | 2.28 MPa | 330 psi | Silicone Property; ASTM D412 | ||
| Elongation at Break | 170 % | 170 % | Silicone Property; ASTM D412 | ||
| Modulus of Elasticity | 0.00159 GPa | 0.230 ksi | Silicone Property; Arlon SQA-TMS-008 | ||
| Poissons Ratio | 0.50 | 0.50 | Approximately, Silicone Property | ||
| Shear Modulus | 0.345 GPa @Strain <=100 % | 50.0 ksi @Strain <=100 % | ASTM D1002 | ||
| Shear Strength | 2.21 MPa | 320 psi | Lap Shear Strength; ASTM D1002 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 5.9 @Frequency 1.00e+6 Hz | 5.9 @Frequency 1.00e+6 Hz | Dk, Silicone Property; IPC TM 650-2.5.5.3 | ||
| Dielectric Strength | 33.5 kV/mm | 850 kV/in | ASTM D149 | ||
| Dissipation Factor | 0.0040 @Frequency 1.00e+6 Hz | 0.0040 @Frequency 1.00e+6 Hz | Df, Silicone Property; IPC TM 650-2.5.5.3 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 128 μm/m-°C | 71.1 μin/in-°F | Silicone Property; ASTM E 831 | ||
| Specific Heat Capacity | 0.900 J/g-°C @Temperature 100 °C | 0.215 BTU/lb-°F @Temperature 212 °F | Silicone Property; ASTM E 1952 | ||
| Thermal Conductivity | 2.30 W/m-K | 16.0 BTU-in/hr-ft2-°F | Product Property; ASTM E 1530 | ||
| 1.40 W/m-K @Temperature 100 °C | 9.72 BTU-in/hr-ft2-°F @Temperature 212 °F | Silicone Property; ASTM E 1530 | |||
| Maximum Service Temperature, Air | 204.0 °C | 399.2 °F | |||
| Minimum Service Temperature, Air | -100 °C | -148 °F | |||
| Glass Transition Temp, Tg | -120 °C | -184 °F | Silicone Property; ASTM D3418 | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 15.0 min | 0.250 hour | After Thermabond? temperature reaches 100°C, Recommended Cure Cycle | ||
| Shelf Life | 6.00 Month @Temperature 4.44 - 10.0 °C | 6.00 Month @Temperature 40.0 - 50.0 °F | From date of manufacture | ||
| Descriptive Properties | |||||
| Color | Gray | ||||
| Plasticity | 2.2 mm | Arlon SQA-TMS-005 | |||
| Total Product Weight (g/m2) | 528 | Arlon SQA-TMS-025 | |||