- 密度 [g/cm3]: 1.75
- 吸水率 [%]: 0.2
- 缺口沖擊強度: 6.94
- 斷裂伸長率 [%]: 138
- 彎曲強度 [MPa]: 55.2
- 彎曲模量 [MPa]: 8.27
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.75 - 1.85 g/cc | 0.0632 - 0.0668 lb/in3 | ASTM D792 |
| Water Absorption | 0.20 - 0.30 % | 0.20 - 0.30 % | ASTM D570 |
| Linear Mold Shrinkage | 0.00 - 0.0010 cm/cm | 0.00 - 0.0010 in/in | Ambient part /mold |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 55.2 - 68.9 MPa | 8000 - 10000 psi | ASTM D638 |
| Elongation at Break | 1.2 - 1.4 % | 1.2 - 1.4 % | ASTM D638 |
| Modulus of Elasticity | 8.96 - 10.3 GPa | 1300 - 1500 ksi | ASTM D638 |
| Flexural Yield Strength | 138 - 179 MPa | 20000 - 26000 psi | ASTM D790 |
| Flexural Modulus | 8.27 - 9.65 GPa | 1200 - 1400 ksi | ASTM D790 |
| Izod Impact, Notched | 6.94 - 9.61 J/cm | 13.0 - 18.0 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.61 - 12.3 J/cm | 18.0 - 23.0 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Flammability, UL94 | HB | HB | FBMV 302 |