- 缺口沖擊強度: 9.5
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.95 g/cc | 1.95 g/cc | |
| Linear Mold Shrinkage | 0.00025 cm/cm | 0.00025 in/in | Polymerization Shrinkage |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 1.2 % | 1.2 % | ASTM D638 |
| Tensile Modulus | 15.0 GPa | 2180 ksi | ASTM D638 |
| Flexural Strength | 210 MPa | 30500 psi | ASTM D790 |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ASTM D790 |
| Poissons Ratio | 0.30 | 0.30 | |
| Shear Modulus | 5.80 GPa | 841 ksi | Calculated |
| Izod Impact, Notched | 9.50 J/cm | 17.8 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 15.0 J/cm | 28.1 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 35.0 μm/m-°C | 19.4 μin/in-°F | Z Direction |
| CTE, linear, Transverse to Flow | 25.0 μm/m-°C | 13.9 μin/in-°F | XY Direction |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft2-°F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 150 °C | 302 °F | Compression Molding |
| Clamp Pressure | 3.45 - 6.89 MPa | 500 - 1000 psi | Molding Pressure |