- 吸水率 [%]: 0.2
- 缺口沖擊強度: 13.9
- 彎曲強度 [MPa]: 82.7
- 彎曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.83 g/cc | 1.83 g/cc | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in | ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 82.7 MPa | 12000 psi | ISO 527 |
| Tensile Modulus | 13.8 GPa | 2000 ksi | tangent; ISO 527 |
| Flexural Strength | 179 MPa | 26000 psi | ISO 178 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | Tangent; ISO 178 |
| Compressive Strength | 310 MPa | 45000 psi | ASTM D695 |
| Poissons Ratio | 0.33 | 0.33 | ISO 527 |
| Shear Modulus | 5.19 GPa | 753 ksi | Calculated |
| Izod Impact, Notched | 13.9 J/cm | 26.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.0 μm/m-°C @Temperature 20.0 °C | 20.0 μin/in-°F @Temperature 68.0 °F | Z-direction; ASTM D696 |
| CTE, linear, Transverse to Flow | 27.0 μm/m-°C @Temperature 20.0 °C | 15.0 μin/in-°F @Temperature 68.0 °F | XY-direction; ASTM D696 |
| Specific Heat Capacity | 1.51 J/g-°C | 0.360 BTU/lb-°F | ASTM D1269E |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft2-°F | ASTM D1269E |
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | ASTM D648 |
| Glass Transition Temp, Tg | 188 °C | 370 °F | ASTM D4065-01 |