- 密度 [g/cm3]: 1.6
- 吸水率 [%]: 1.1
- 缺口沖擊強度: 5.3
- 彎曲強度 [MPa]: 72.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 72.0 MPa | 10400 psi | ASTM D638 |
| Compressive Strength | 97.0 MPa | 14100 psi | ASTM D695 |
| Izod Impact, Notched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.2 @Frequency 1e+6 Hz | 4.2 @Frequency 1e+6 Hz | ASTM D150 |
| 6.4 @Frequency 60 Hz | 6.4 @Frequency 60 Hz | ASTM D150 | |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | Perpendicular, Short-term, in air; ASTM D149 |
| Dissipation Factor | 0.033 @Frequency 1e+6 Hz | 0.033 @Frequency 1e+6 Hz | ASTM D150 |
| 0.070 @Frequency 60 Hz | 0.070 @Frequency 60 Hz | ASTM D150 | |
| Arc Resistance | 139 sec | 139 sec | ASTM D495 |
| Comparative Tracking Index | >= 500 V | >= 500 V | UL746A |
| Hot Wire Ignition, HWI | 102 sec | 102 sec | 0.058 in, UL746A |
| High Amp Arc Ignition, HAI | 200 arcs | 200 arcs | UL746A |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 mm/min | 0.000 in/min | UL746A |
| Thermal Properties | Metric | English | Comments |
| UL RTI, Electrical | 200 °C | 392 °F | 0.058 in, UL746B |
| UL RTI, Mechanical with Impact | 200 °C | 392 °F | 0.058 in, UL746B |
| Flammability, UL94 | HB | HB | |
| Oxygen Index | 21.8 % | 21.8 % | ASTM D2862 |