- 拉伸強度 [MPa]: 400.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | |
| Moisture Absorption at Equilibrium | 0.31 % @Thickness 1.57 mm | 0.31 % @Thickness 0.0620 in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 80 - 100 @Thickness 1.57 mm | 80 - 100 @Thickness 0.0620 in | |
| Tensile Strength, Yield | 400 MPa @Thickness 3.17 mm | 58000 psi @Thickness 0.125 in | CW |
| 427 MPa @Thickness 3.17 mm | 62000 psi @Thickness 0.125 in | LW | |
| Flexural Strength | 386 MPa @Thickness 1.57 mm | 56000 psi @Thickness 0.0620 in | CW |
| 386 MPa @Thickness 1.57 mm | 56000 psi @Thickness 0.0620 in | LW | |
| Compressive Strength | 545 MPa @Thickness 12.7 mm | 79000 psi @Thickness 0.500 in | Flatwise |
| Izod Impact, Unnotched | 4.27 J/cm @Thickness 12.7 mm | 8.00 ft-lb/in @Thickness 0.500 in | CW, E-48/50 |
| 5.82 J/cm @Thickness 12.7 mm | 10.9 ft-lb/in @Thickness 0.500 in | LW, E-48/50 | |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 3.91 @Thickness 1.57 mm | 3.91 @Thickness 0.0620 in | Permittivity, Cond D-24/23 |
| Dielectric Strength | 19.7 kV/mm @Thickness 1.57 mm | 500 kV/in @Thickness 0.0620 in | D-48/50 |
| 25.6 kV/mm @Thickness 1.57 mm | 650 kV/in @Thickness 0.0620 in | Condition - A | |
| Dielectric Breakdown | 47000 V @Thickness 1.57 mm | 47000 V @Thickness 0.0620 in | Condition A |
| 54000 V @Thickness 1.57 mm | 54000 V @Thickness 0.0620 in | D-48/50 | |
| Dissipation Factor | 0.0275 @Thickness 1.57 mm | 0.0275 @Thickness 0.0620 in | Cond D-24/23 |
| Arc Resistance | 121 sec @Thickness 3.17 mm | 121 sec @Thickness 0.125 in | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 36.3 μm/m-°C @Thickness 1.57 mm, Temperature 40.0 - 105 °C | 20.2 μin/in-°F @Thickness 0.0620 in, Temperature 104 - 221 °F | x-axis |
| 262 μm/m-°C @Thickness 1.57 mm, Temperature 105 - 155 °C | 146 μin/in-°F @Thickness 0.0620 in, Temperature 221 - 311 °F | x-axis | |
| Maximum Service Temperature, Air | 180 °C | 356 °F | Maximum Operating Temperature |
| Glass Transition Temp, Tg | 145 °C | 293 °F | Tg |
| Flammability, UL94 | V-0 | V-0 | |