- 拉伸強(qiáng)度 [MPa]: 10.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 10.9 MPa @Temperature 25.0 °C | 1580 psi @Temperature 77.0 °F | Quasi tensile strength |
| 57.9 MPa @Temperature 25.0 °C | 8400 psi @Temperature 77.0 °F | Quasi tensile strength | |
| 75.8 MPa @Temperature 25.0 °C | 11000 psi @Temperature 77.0 °F | 90°, Dry | |
| 931 MPa @Temperature 25.0 °C | 135000 psi @Temperature 77.0 °F | Quasi tensile strength | |
| 2760 MPa @Temperature 25.0 °C | 400000 psi @Temperature 77.0 °F | 0°, Dry | |
| Elongation at Yield | 1.0 % @Temperature 25.0 °C | 1.0 % @Temperature 77.0 °F | 90°, Dry |
| 1.64 % @Temperature 25.0 °C | 1.64 % @Temperature 77.0 °F | 0°, Dry | |
| Tensile Modulus | 8.34 GPa @Temperature 25.0 °C | 1210 ksi @Temperature 77.0 °F | 90°, Dry |
| 159 GPa @Temperature 25.0 °C | 23100 ksi @Temperature 77.0 °F | 0°, Dry | |
| Compressive Yield Strength | 228 MPa @Temperature 25.0 °C | 33100 psi @Temperature 77.0 °F | After 3000 in-inlb/in impact |
| 248 MPa @Temperature 104 °C | 36000 psi @Temperature 219 °F | Open hole compression, Wet | |
| 255 MPa @Temperature 82.0 °C | 37000 psi @Temperature 180 °F | Open hole compression, Wet | |
| 290 MPa @Temperature 25.0 °C | 42100 psi @Temperature 77.0 °F | Open hole compression, Dry | |
| 303 MPa @Temperature 25.0 °C | 43900 psi @Temperature 77.0 °F | After 2500 in-inlb/in impact | |
| 324 MPa @Temperature 25.0 °C | 47000 psi @Temperature 77.0 °F | After 2000 in-inlb/in impact | |
| 345 MPa @Temperature 25.0 °C | 50000 psi @Temperature 77.0 °F | After 1500 in-inlb/in impact | |
| 462 MPa @Temperature 25.0 °C | 67000 psi @Temperature 77.0 °F | After 500 in-inlb/in impact | |
| 586 MPa @Temperature 25.0 °C | 85000 psi @Temperature 77.0 °F | Unimpacted | |
| 1100 MPa @Temperature 82.0 °C | 160000 psi @Temperature 180 °F | 0°, Wet | |
| 1280 MPa @Temperature 121 °C | 186000 psi @Temperature 250 °F | 0°, Dry | |
| 1380 MPa @Temperature 82.0 °C | 200000 psi @Temperature 180 °F | 0°, Dry | |
| 1620 MPa @Temperature 25.0 °C | 235000 psi @Temperature 77.0 °F | 0°, Dry | |
| Compressive Modulus | 143 GPa @Temperature 82.0 °C | 20700 ksi @Temperature 180 °F | 0°, Wet |
| 145 GPa @Temperature 82.0 °C | 21000 ksi @Temperature 180 °F | 0°, Dry | |
| 148 GPa @Temperature 25.0 °C | 21500 ksi @Temperature 77.0 °F | 0°, Dry | |
| 150 GPa @Temperature 104 °C | 21800 ksi @Temperature 219 °F | 0°, Wet | |
| 152 GPa @Temperature 121 °C | 22000 ksi @Temperature 250 °F | 0°, Dry | |
| Shear Modulus | 5.86 GPa @Temperature 25.0 °C | 850 ksi @Temperature 77.0 °F | In-Plane +/- 45 tensile shear; Dry |
| Shear Strength | 40.0 MPa @Temperature 129 °C | 5800 psi @Temperature 264 °F | Short Beam, Wet |
| 56.5 MPa @Temperature 121 °C | 8190 psi @Temperature 250 °F | Short Beam, Wet | |
| 68.9 MPa @Temperature 121 °C | 9990 psi @Temperature 250 °F | Short Beam, Dry | |
| 68.9 MPa @Temperature 82.0 °C | 9990 psi @Temperature 180 °F | Short Beam, Wet | |
| 79.3 MPa @Temperature 82.0 °C | 11500 psi @Temperature 180 °F | Short Beam, Dry | |
| 100 MPa @Temperature 25.0 °C | 14500 psi @Temperature 77.0 °F | Short Beam, Dry | |
| 117 MPa @Temperature 25.0 °C | 17000 psi @Temperature 77.0 °F | In-Plane +/- 45 tensile shear; Dry | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 93.3 °C | 200 °F | Epoxy Matrix Limit |