| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Storage Temperature | 4.00 °C | 39.2 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 42.8 MPa | 6210 psi | |||
| Elongation at Break | 1.2 % | 1.2 % | |||
| Tensile Modulus | 4.45 GPa | 645 ksi | |||
| Compressive Strength | 93.1 MPa | 13500 psi | |||
| Compressive Modulus | 2.53 GPa | 367 ksi | |||
| Adhesive Bond Strength | 13.8 MPa @Temperature 93.0 °C | 2000 psi @Temperature 199 °F | Tensile Lap Shear | ||
| 19.3 MPa @Temperature -55.0 °C | 2800 psi @Temperature -67.0 °F | Tensile Lap Shear | |||
| 21.4 MPa @Temperature 25.0 °C | 3100 psi @Temperature 77.0 °F | Tensile Lap Shear | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 149 °C | 300 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 60.0 min @Temperature 93.0 °C | 1.00 hour @Temperature 199 °F | |||
| 7200 - 10100 min @Temperature 25.0 °C | 120 - 168 hour @Temperature 77.0 °F | ||||
| Pot Life | 40 min | 40 min | |||
| Descriptive Properties | |||||
| Consistency | Thixotropic | ||||
| Form | 2 parts | ||||
| Mix Ratio, Part A:Part B | 100:33 | ||||
| Peel Strength | Nil | ||||