- 密度 [g/cm3]: 1.12
- 彎曲模量 [MPa]: 19.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 - 1.13 g/cc | 0.0405 - 0.0408 lb/in3 | |||
| Viscosity | 950 - 975 cP | 950 - 975 cP | ASTM D2293 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 88 | 88 | Cured; ASTM D2240 | ||
| Tensile Strength at Break | 312.51 MPa | 45326 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Elongation at Break | 1.93 % | 1.93 % | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D638 | ||
| Tensile Modulus | 17.4 GPa | 2530 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content. | ||
| Flexural Strength | 450.28 MPa | 65308 psi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Flexural Modulus | 19.5 GPa | 2830 ksi | Property derived with 10 Ply Laminate, hand Lay-up, Style 181 Glass Fabric, 55% Glass Content.; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 67.1 μm/m-°C @Temperature 37.8 - 65.6 °C | 37.3 μin/in-°F @Temperature 100 - 150 °F | ASTM D696 | ||
| Glass Transition Temp, Tg | 82.2 °C | 180 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Pot Life | 20 min | 20 min | Value for 4 fl. Oz. at 77°F; ASTM D2471 | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 100:23 | Resin:Hardener by Weight | |||
| 4.3:1 | Resin:Hardener by Volume | ||||