- 密度 [g/cm3]: 1.8
- 彎曲強度 [MPa]: 81.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in3 | |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | |
| Viscosity | 50000 cP | 50000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 95 | 95 | |
| Tensile Strength, Ultimate | 81.4 MPa | 11800 psi | |
| Elongation at Break | 2.0 % | 2.0 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 68.0 μm/m-°C @Temperature 20.0 °C | 37.8 μin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 2.59 W/m-K | 18.0 BTU-in/hr-ft2-°F | |
| Maximum Service Temperature, Air | 371 °C | 700 °F | |
| Shrinkage | 0.10 % | 0.10 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 240 - 360 min | 4.00 - 6.00 hour | at 250°F |