- 密度 [g/cm3]: 3.8
- 彎曲強度 [MPa]: 44.8
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.80 g/cc | 0.137 lb/in3 | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | |
| Viscosity | 15000 cP | 15000 cP | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 70 | 70 | |
| Tensile Strength, Ultimate | 44.8 MPa | 6500 psi | |
| Elongation at Break | 0.20 % | 0.20 % | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 0.000080 ohm-cm | 0.000080 ohm-cm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 μm/m-°C @Temperature 20.0 °C | 30.0 μin/in-°F @Temperature 68.0 °F | |
| Thermal Conductivity | 7.20 W/m-K | 50.0 BTU-in/hr-ft2-°F | |
| Maximum Service Temperature, Air | 260 °C | 500 °F | |
| Shrinkage | 0.20 % | 0.20 % | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min | 0.333 hour | at 250°F |