- 彎曲強度 [MPa]: 59.6
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Viscosity | 160000 cP | 160000 cP | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 86 | 86 | |||
| Tensile Strength, Ultimate | 59.6 MPa | 8650 psi | after optimum cure | ||
| Elongation at Break | 2.4 % | 2.4 % | |||
| Adhesive Bond Strength | 34.1 MPa | 4950 psi | Steel-Steel; after optimum cure | ||
| 19.3 MPa @Temperature -54.4 °C | 2800 psi @Temperature -66.0 °F | Aluminum-Aluminum tensile shear | |||
| 27.9 MPa @Temperature 82.2 °C | 4050 psi @Temperature 180 °F | Aluminum-Aluminum tensile shear | |||
| 42.1 MPa @Temperature 25.0 °C | 6100 psi @Temperature 77.0 °F | Aluminum-Aluminum tensile shear | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 53.0 μm/m-°C @Temperature 20.0 °C | 29.4 μin/in-°F @Temperature 68.0 °F | |||
| Maximum Service Temperature, Air | 204 °C | 400 °F | After 350°F minimum cure temp. | ||
| Glass Transition Temp, Tg | 130 °C | 266 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 177 °C | 350 °F | Optimum cure is 2 hr. @ 350°F | ||
| 260 °C | 500 °F | Fast cure is 10 min. @ 500°F | |||
| Pot Life | 99999 min | 99999 min | Indefinite working life at 25°C (100 g) | ||
| Descriptive Properties | |||||
| Color | Amber | ||||
| Mix Ratio | 1 Part | ||||