- 密度 [g/cm3]: 2.01
- 吸水率 [%]: 0.18
- 缺口沖擊強(qiáng)度: 0.2
- 彎曲模量 [MPa]: 19.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.900 g/cc | 0.0325 lb/in3 | ASTM D1895 | ||
| Density | 2.01 g/cc | 0.0726 lb/in3 | ASTM D792 | ||
| Water Absorption | 0.18 % @Temperature 50.0 °C, Time 173000 sec | 0.18 % @Temperature 122 °F, Time 48.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 68.0 MPa | 9860 psi | ASTM D638 | ||
| Flexural Strength | 114 MPa | 16500 psi | at rupture; ASTM D790 | ||
| Flexural Modulus | 19.0 GPa | 2760 ksi | ASTM D790 | ||
| Compressive Strength | 235 MPa | 34100 psi | ASTM D695 | ||
| Izod Impact, Notched | 0.200 J/cm | 0.375 ft-lb/in | ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 4.6 @Frequency 1.00e+6 Hz | 4.6 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Dielectric Strength | 16.0 kV/mm @Frequency 60.0 Hz | 406 kV/in @Frequency 60.0 Hz | step-by-step, wet; ASTM D149 | ||
| 18.5 kV/mm @Frequency 60.0 Hz | 470 kV/in @Frequency 60.0 Hz | short time, wet; ASTM D149 | |||
| Dissipation Factor | 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | wet; ASTM D150 | ||
| Arc Resistance | 180 sec | 180 sec | ASTM D495 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 282 °C | >= 540 °F | Post Baked; ASTM D648A | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Form | Granular | ||||
| Molding Method | Compression | ||||
| Transfer | |||||