- 缺口沖擊強度: 0.907
- 拉伸強度 [MPa]: 125.0
- 彎曲模量 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.26 g/cc | 1.26 g/cc | Method A; ASTM D792 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | ASTM D638 |
| Tensile Strength, Yield | 125 MPa | 18100 psi | ASTM D638 |
| Elongation at Break | 1.4 % | 1.4 % | ASTM D638 |
| Elongation at Yield | 1.4 % | 1.4 % | ASTM D638 |
| Tensile Modulus | 11.5 GPa | 1670 ksi | ASTM D638 |
| Flexural Strength | 200 MPa | 29000 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 0.907 J/cm @Thickness 3.18 mm | 1.70 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Unnotched | 5.93 J/cm @Thickness 3.18 mm | 11.1 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 | 3.81 ft-lb/in2 | ISO 180 |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | ISO 180 |
| Falling Dart Impact | 9.61 J | 7.09 ft-lb | ASTM D3763 |
| Impact Test | 2.56 J | 1.89 ft-lb | Multi-Axial Instrumented Impact Energy; ISO 6603-2 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 304 - 321 °C | 579 - 610 °F | |
| Mold Temperature | 82.2 - 149 °C | 180 - 300 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4 hour | 4 hour | |
| Back Pressure | 0.172 - 0.345 MPa | 24.9 - 50.0 psi | |