- 密度 [g/cm3]: 1.22
- 吸水率 [%]: 0.01
- 缺口沖擊強度: 0.96
- 拉伸強度 [MPa]: 92.0
- 彎曲強度 [MPa]: 92.0
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ASTM Data |
| Water Absorption | 0.010 % | 0.010 % | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 92.0 MPa | 13300 psi | ASTM Data |
| Tensile Strength, Yield | 92.0 MPa | 13300 psi | ASTM Data |
| Tensile Modulus | 7.58 GPa | 1100 ksi | ASTM Data |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM Data |
| Electrical Properties | Metric | English | Comments |
| Dielectric Strength | 21.8 kV/mm | 554 kV/in | |
| Dissipation Factor | 0.0010 | 0.0010 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 29.8 μm/m-°C @Temperature 20.0 °C | 16.6 μin/in-°F @Temperature 68.0 °F | ASTM data |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 263 °C | 505 °F | |