- 密度 [g/cm3]: 1.21
- 成型收縮率 [%]: 0.001
- 缺口沖擊強(qiáng)度: 14.0
- 拉伸強(qiáng)度 [MPa]: 110.0
- 彎曲模量 [MPa]: 8.50
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | ISO 1183 B |
| Filler Content | 30 % | 30 % | Glass |
| Moisture Absorption | 0.0100 % | 0.0100 % | 24 hours, 50% RH |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 1.60 mm | 0.0010 - 0.0030 in/in @Thickness 0.0630 in | ISO 294 |
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0040 in/in @Thickness 0.126 in | ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.010 cm/cm @Thickness 3.20 mm | 0.0020 - 0.010 in/in @Thickness 0.126 in | ISO 294 |
| 0.0020 - 0.010 cm/cm @Thickness 1.60 mm | 0.0020 - 0.010 in/in @Thickness 0.0630 in | ISO 294 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ISO 527 |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527 |
| Tensile Modulus | 8.50 GPa | 1230 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 8.50 GPa | 1230 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m2 @Temperature 23.0 °C | 6.66 ft-lb/in2 @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | ISO 180 |
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature 23.0 °C | 19.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 1.20 J/cm2 @Temperature 23.0 °C | 5.71 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.9e+12 ohm-cm | 5.9e+12 ohm-cm | IEC 93 |
| Dielectric Constant | 3.1 | 3.1 | IEC 250 |
| Dielectric Strength | 28.0 kV/mm | 711 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | ISO 75A |
| Vicat Softening Point | 260 °C | 500 °F | A/10N; ISO 306 |
| Flammability, UL94 | HB | HB | |
| Glow Wire Test | 650 °C @Thickness 1.00 mm | 1200 °F @Thickness 0.0394 in | IEC 695-2-1 |
| 650 °C @Thickness 2.00 mm | 1200 °F @Thickness 0.0787 in | IEC 695-2-1 | |
| 750 °C @Thickness 3.00 mm | 1380 °F @Thickness 0.118 in | IEC 695-2-1 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 290 - 330 °C | 554 - 626 °F | pre-drying not required |
| Mold Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |
| 130 - 150 °C | 266 - 302 °F | for optimal gloss and heat resistance | |