- 密度 [g/cm3]: 1.7
- 缺口沖擊強度: 18.0
- 彎曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.70 g/cc | 0.0614 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0050 cm/cm | 0.0050 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 77 | 77 | ISO 2039-2 |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ISO 527-2/1A |
| Elongation at Break | 1.2 % | 1.2 % | 5 mm/min; ISO 527-2/1A |
| Tensile Modulus | 17.0 GPa | 2470 ksi | 1 mm/min; ISO 527-2/1A |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m2 | 8.57 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 27.0 kJ/m2 | 12.8 ft-lb/in2 | ISO 180/1U |
| Charpy Impact Unnotched | 2.40 J/cm2 | 11.4 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | IEC 60250 |
| 4.1 @Frequency 100 Hz | 4.1 @Frequency 100 Hz | IEC 60250 | |
| Dissipation Factor | 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 |
| 0.020 @Frequency 1e+6 Hz | 0.020 @Frequency 1e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.00 μm/m-°C @Temperature 20.0 °C | 2.22 μin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 18.0 μm/m-°C @Temperature 20.0 °C | 10.0 μin/in-°F @Temperature 68.0 °F | ISO 11359-2 |
| Melting Point | 330 °C | 626 °F | ISO 11357-1,2,3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 306 °C | 583 °F | ISO 75-1, -2 |
| Deflection Temperature at 8.0 MPa | 251 °C | 484 °F | ISO 75-1, -2 |
| Vicat Softening Point | 224 °C | 435 °F | ISO 306 |
| Flammability, UL94 | V-0 | V-0 | thickness h |
| Oxygen Index | 50 % | 50 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 315 - 325 °C | 599 - 617 °F | |
| Middle Barrel Temperature | 325 - 335 °C | 617 - 635 °F | |
| Front Barrel Temperature | 330 - 340 °C | 626 - 644 °F | |
| Nozzle Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | |