- 缺口沖擊強度: 0.27
- 彎曲模量 [MPa]: 12.2
- 熱變形溫度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.52 g/cc | 1.52 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm | 0.0070 - 0.010 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 93.8 MPa | 13600 psi | ASTM D638 | ||
| Elongation at Break | 1.0 % | 1.0 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 15.8 GPa | 2290 ksi | Type I, 5.1 mm/min; ASTM D638 | ||
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 | ||
| Flexural Modulus | 12.2 GPa | 1770 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.270 J/cm @Thickness 3.18 mm, Temperature 23.0 °C | 0.506 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 | ||
| Static Decay | 0.0020 sec | 0.0020 sec | (Mil-B-81705C), 12% RH, 500 kV to 50 kV | ||
| Shielding Effectiveness | 30 - 80 dB @Frequency 2.00e+7 - 1.80e+10 Hz | 30 - 80 dB @Frequency 2.00e+7 - 1.80e+10 Hz | 1/8 thickness | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C @Thickness 6.35 mm | 500 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C @Thickness 6.35 mm | 403 °F @Thickness 0.250 in | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 299 - 316 °C | 570 - 601 °F | |||
| Descriptive Properties | |||||
| Features | Antistatic | ||||
| Conductive | |||||
| Electrically Conductive | |||||
| Electromagnetic Shielding (EMI) | |||||
| Radio Frequency Shielding (RFI) | |||||
| Statically Conductive | |||||
| Filler / Reinforcement | Carbon Fiber Reinforcement, 20% Filler by Weight | ||||
| Forms | Pellets | ||||
| Generic Material | LCP | ||||
| Generic Name | Liquid Crystal Polymer (LCP) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Aerospace Applications | ||||
| Automotive Electronics | |||||
| Business Equipment | |||||
| Computer Components | |||||
| Connectors | |||||
| Electrical Housing | |||||
| Electrical/Electronic Applications | |||||
| Housings | |||||