- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.886
- 拉伸強(qiáng)度 [MPa]: 33.0
- 彎曲模量 [MPa]: 1.83
- 硬度: 97.0
- 熱變形溫度 [℃]: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.886 - 0.926 g/cc | 0.0320 - 0.0335 lb/in3 | ASTM D1505 |
| Water Absorption | <= 0.010 % | <= 0.010 % | 24 hours; ASTM D570 |
| Linear Mold Shrinkage | 0.010 - 0.025 cm/cm | 0.010 - 0.025 in/in | ASTM D955 |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 97 | 97 | ASTM D785 |
| Tensile Strength, Yield | 33.0 MPa | 4790 psi | ASTM D638 |
| Elongation at Break | >= 25 % | >= 25 % | ASTM D638 |
| Flexural Modulus | 1.83 GPa | 265 ksi | ASTM D790A |
| Izod Impact, Notched | NB @Diameter 3.17 mm | NB @Diameter 0.125 in | bar; ASTM D256 |
| 0.350 J/cm @Diameter 3.17 mm, Temperature -20.0 °C | 0.656 ft-lb/in @Diameter 0.125 in, Temperature -4.00 °F | bar; ASTM D256 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 118 °C | 244 °F | ASTM D648 |