- 缺口沖擊強度: 0.587
- 拉伸強度 [MPa]: 32.69
- 彎曲模量 [MPa]: 1.17
- 硬度: 108.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Index of Compound | 12 g/10 min @Temperature 230 °C | 12 g/10 min @Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 108 | 108 | ASTM D785 |
| Tensile Strength, Yield | 32.69 MPa | 4742 psi | 50 mm/min; ASTM D638 |
| Elongation at Yield | 12 % | 12 % | 50 mm/min; ASTM D638 |
| Flexural Modulus | 1.17 GPa | 170 ksi | 1.3 mm/min, 1% Secant; ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Temperature 22.8 °C | 1.10 ft-lb/in @Temperature 73.0 °F | ASTM D256 |