- 熔體流動速率 [g/10min]: 31.0
- 缺口沖擊強度: 0.785
- 斷裂伸長率 [%]: 58.8
- 彎曲模量 [MPa]: 1.86
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0070 cm/cm | 0.0050 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 31 g/10 min | 31 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 49.0 MPa | 7110 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Yield Strength | 58.8 MPa | 8530 psi | ASTM D790 |
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 |
| Izod Impact, Notched | 0.785 J/cm @Thickness 3.17 mm | 1.47 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | |