- 熔體流動速率 [g/10min]: 3.2
- 密度 [g/cm3]: 1.19
- 缺口沖擊強度: 0.187
- 透光率 [%]: 92.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ASTM D-792 |
| Linear Mold Shrinkage | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | ASTM D-955 |
| Melt Flow | 3.2 g/10 min @Load 3.80 kg, Temperature 230 °C | 3.2 g/10 min @Load 8.38 lb, Temperature 446 °F | ASTM D-1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength | 71.0 MPa | 10300 psi | ASTM D-638 |
| Elongation at Break | 4.2 % | 4.2 % | ASTM D-638 |
| Modulus of Elasticity | 3.65 GPa | 529 ksi | ASTM D-638 |
| Flexural Strength | 121 MPa | 17600 psi | ASTM D-790 |
| Izod Impact, Notched | 0.187 J/cm @Thickness 6.35 mm | 0.350 ft-lb/in @Thickness 0.250 in | ASTM D-256 |
| Gardner Impact | 0.226 J @Thickness 3.17 mm | 0.167 ft-lb @Thickness 0.125 in | Falling Weight; ASTM D-3029 GB |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 30.0 μm/m-°C | 16.7 μin/in-°F | ASTM D-696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ASTM D-648 |
| Vicat Softening Point | 113 °C | 235 °F | ASTM D-1525 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 1.0 % | <= 1.0 % | ASTM D-1003 |
| Transmission, Visible | 92 % @Thickness 3.17 mm | 92 % @Thickness 0.125 in | Luminous; ASTM D-1003 |
| UV Transmittance | 49.5 % @Thickness 3.17 mm, Wavelength 270 nm | 49.5 % @Thickness 0.125 in, Wavelength 270 nm | ASTM D-1003 |
| 88.5 % @Thickness 3.17 mm, Wavelength 300 nm | 88.5 % @Thickness 0.125 in, Wavelength 300 nm | ASTM D-1003 | |