- 密度 [g/cm3]: 1.38
- 缺口沖擊強度: 0.96
- 斷裂伸長率 [%]: 68.0
- 彎曲強度 [MPa]: 50.0
- 彎曲模量 [MPa]: 2.617
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 50.0 MPa | 7250 psi | ASTM D638 |
| Elongation at Break | 175 % | 175 % | ASTM D638 |
| Flexural Yield Strength | 68.0 MPa | 9860 psi | ASTM D790 |
| Flexural Modulus | 2.617 GPa | 379.6 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm @Temperature 23.0 °C | 1.80 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 160 - 171 °C | 320 - 340 °F | Barrel Temp |
| Middle Barrel Temperature | 160 - 171 °C | 320 - 340 °F | |
| Adapter Temperature | 171 - 177 °C | 340 - 350 °F | |
| Die Temperature | 171 - 177 °C | 340 - 350 °F | |
| Dry Time | 0.0 hour | 0.0 hour | Drying typically not required |