- 熔體流動(dòng)速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.11
- 缺口沖擊強(qiáng)度: 9.0
- 拉伸強(qiáng)度 [MPa]: 51.0
- 斷裂伸長率 [%]: 93.0
- 彎曲模量 [MPa]: 2.70
- 熱變形溫度 [℃]: 71.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | |
| Apparent Bulk Density | 0.680 g/cc | 0.0246 lb/in3 | |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 12.5 kg, Temperature 200 °C | 3.0 g/10 min @Load 27.6 lb, Temperature 392 °F | 2 mm x 8 mm |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 45 | 45 | |
| Tensile Strength, Yield | 51.0 MPa | 7400 psi | |
| Elongation at Break | 4.0 % | 4.0 % | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | |
| Flexural Modulus | 2.70 GPa | 392 ksi | |
| Izod Impact, Notched | 9.00 J/cm | 16.9 ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 1.30 J/g-°C | 0.311 BTU/lb-°F | |
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft2-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 71.0 °C | 160 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |
| Vicat Softening Point | 77.0 °C | 171 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 200 °C | 392 °F | |