- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.927
- 拉伸強度 [MPa]: 9.0
- 彎曲強度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in3 | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 46 | 46 | ASTM D2240 |
| Tensile Strength, Ultimate | 19.0 MPa | 2760 psi | ASTM D638 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ASTM D638 |
| Film Elongation at Break, MD | 180 % | 180 % | ASTM D882 |
| Film Elongation at Break, TD | 260 % | 260 % | ASTM D882 |
| Elongation at Break | 1000 % | 1000 % | ASTM D638 |
| Modulus of Elasticity | 0.235 GPa | 34.1 ksi | Secant; ASTM D638 |
| Secant Modulus, MD | 0.131 GPa | 19.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.145 GPa | 21.0 ksi | ASTM D882 |
| Dart Drop | 9.84 g/micron | 250 g/mil | ASTM D1709 |
| Dart drop Test | 250 g | 0.551 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 25.0 MPa | 3630 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 88.0 °C | 190 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 6.0 % | 6.0 % | ASTM D1003 |
| Gloss | 65 % | 65 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 204 - 215 °C | 399 - 419 °F | |