- 熔體流動速率 [g/10min]: 3.1
- 密度 [g/cm3]: 0.952
- 彎曲強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 0.0190
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.952 g/cc | 0.0344 lb/in3 | Exxon Method |
| Environmental Stress Crack Resistance | >= 500 hour | >= 500 hour | F50, Condition A; ASTM D1693 |
| Melt Flow | 3.1 g/10 min | 3.1 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 72 | 72 | ASTM D2240 |
| Hardness, Shore D | 23 | 23 | ASTM D2240 |
| Tensile Strength, Ultimate | 14.0 MPa | 2030 psi | ASTM D638 |
| Elongation at Break | >= 800 % | >= 800 % | ASTM D638 |
| Flexural Modulus | 0.0190 GPa | 2.76 ksi | 1% Secant, ASTM D790 |
| Tensile Impact Strength | 815 kJ/m2 | 388 ft-lb/in2 | 23°C; ASTM D-1822 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 70.0 °C | 158 °F | Exxon Method |
| Vicat Softening Point | 48.0 °C | 118 °F | 1000g; ASTM D-1525 |