- 熔體流動速率 [g/10min]: 22.0
- 密度 [g/cm3]: 0.941
- 彎曲模量 [MPa]: 0.0434
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in3 | ASTM D1505 |
| Particle Mesh Size | 35 Mesh | 35 Mesh | Irregular shape. ETM = Equistar Test Method; ETM Malvern |
| Melt Flow | 22 g/10 min | 22 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength at Break | 9.38 MPa | 1360 psi | ASTM D638 |
| Elongation at Break | 730 % | 730 % | ASTM D638 |
| Flexural Modulus | 0.0434 GPa | 6.30 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 86.0 °C | 187 °F | ASTM D3418 |
| Vicat Softening Point | 60.0 °C | 140 °F | ASTM D1525 |
| Brittleness Temperature | -76.0 °C | -105 °F | ASTM D746 |