- 熔體流動速率 [g/10min]: 1.2
- 密度 [g/cm3]: 0.94
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.940 g/cc | 0.0340 lb/in3 | ASTM D792 |
| Moisture Vapor Transmission | 0.590 cc-mm/m2-24hr-atm @Thickness 0.0254 mm | 1.50 cc-mil/100 in2-24hr-atm @Thickness 0.00100 in | g-mm/m2-day; based on film thickness; ASTM E96; ASTM E96 |
| Oxygen Transmission | 177 cc-mm/m2-24hr-atm @Thickness 0.0254 mm | 450 cc-mil/100 in2-24hr-atm @Thickness 0.00100 in | film; ASTM D3985 |
| Melt Flow | 1.2 g/10 min | 1.2 g/10 min | Condition not noted.; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 450 % | 450 % | MD-TD Average; ASTM D882 |
| Film Elongation at Break, TD | 450 % | 450 % | MD-TD Average; ASTM D882 |
| Impact | 15.1 | 15.1 | J/mm Spencer Impact; Average of MD and TD; ASTM D3420 |
| Elmendorf Tear Strength, MD | 2.05 g/micron | 52.0 g/mil | Average of MD and TD; ASTM D1922 |
| Film Tensile Strength at Break, MD | 21.4 MPa | 3100 psi | MD-TD Average; ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 82.0 °C | 180 °F | Freezing Point via DSC/ASTM D3418 |
| 99.0 °C | 210 °F | Upon Melting via DSC/ASTM D3418 | |
| Vicat Softening Point | 84.0 °C | 183 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D1003 |
| Gloss | 17 % | 17 % | 20°; ASTM D2457 |