Stapron? E EM 605|(PC+PET)|Mitsubishi EP

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
熔體體積流動速率(Melt volume-flow rate) (MVR)	7	cm3/10min	ISO 1133
溫度(Temperature)	280	°C	ISO 1133
負載(Load)	1.2	kg	ISO 1133
成型收縮(Molding shrinkage) (parallel)	0.7	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
拉伸模量(Tensile Modulus)	2200	MPa	ISO 527-1/-2
屈服應力(Yield stress)	55	MPa	ISO 527-1/-2
屈服應變(Yield strain)	6	%	ISO 527-1/-2
斷裂拉伸應變(Nominal strain at break)	>50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	N	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	55	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	25	kJ/m2	ISO 179/1eA

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	120	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	130	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	80	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	80	E-6/K	ISO 11359-1/-2
燃燒性(球壓痕硬度(Burning behav)). at 1.5 mm nom. thickn.	HB	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10

流變計算屬性(Rheological calculation properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
密度(Density) of melt	1080	kg/m3	-
熔體熱導率(Thermal conductivity of melt)	0.162	W/(m K)	-
規格的熱容融化(Spec. heat capacity of melt)	2110	J/(kg K)	-
Eff. thermal diffusivity	7.14E-8	m2/s	-
噴射溫度(Ejection temperature)	120	°C	-

Test specimen production	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據(ISO數據(CAMPUS/ISO) Data)
Injection Molding, melt temperature	280	°C	ISO 294
Injection Molding, mold temperature	90	°C	ISO 10724

Diagrams .