Lexan XHT8141|PC|沙特基礎物性表: Lexan XHT8141|PC|沙特基礎物性表及特性介紹,Lexan XHT8141|PC|沙特基礎注塑參數詳情,如需Lexan XHT8141|PC|沙特基礎下載, 可到相關下載區下載

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
熔體流動指數(Melt Flow Index)	7.5	g/10min	ASTM D 1238
模具收縮(Mold Shrinkage) (MD)	0.008	mm/mm	ASTM D 955
密度(Density) (73°F)	1220	kg/m3	ASTM D 792

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
拉伸模量(Tensile Modulus)	2847.53	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	80	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	64.8	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	7.5	%	ASTM D 638
斷裂伸長率(Elongation at Break)	20	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	2695.85	MPa	ASTM D 790
抗彎強度(Flexural Strength)	130	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/8 in)	0.0854	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	0.048	kJ/m	ASTM D 256
溫度(Temperature)	-30	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	69.8	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	69.8	E-6/K	ASTM D 696
DTUL @ 66 psi	208	°C	ASTM D 648
DTUL @ 264 psi	192	°C	ASTM D 648
Vicat 溫度(Temperature)	212	°C	ASTM D 1525

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
絕緣強度(Dielectric Strength) (Short Time)	23	kV/mm	ASTM D 149
耗散因數(Dissipation Factor) (60 Hz)	0.05	-	ASTM D 150
耗散因數(Dissipation Factor) (1 MHz)	0.01	-	ASTM D 150
表面電阻率(Surface Resistivity)	4.50E13	Ohm	ASTM D 257
體積電阻率(Volume Resistivity)	>1E15	Ohm*cm	ASTM D 257

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsHeat stabilized or stable to heatFeaturesCopolymerRegional AvailabilityNorth America, Europe, Asia Pacific, Near East/AfricaDisclaimerCopyright M-Base .

關鍵詞:
PC
SABIC_IP
Lexan XHT8141

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-97897.html

免責聲明: 本文 Lexan XHT8141|PC|沙特基礎 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡