Lexan ML7686|PC|沙特基礎

Lexan ML7686|PC|沙特基礎物性表: Lexan ML7686|PC|沙特基礎物性表及特性介紹,Lexan ML7686|PC|沙特基礎注塑參數詳情,如需Lexan ML7686|PC|沙特基礎下載, 可到相關下載區下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
熔體體積流動速率(Melt volume-flow rate) (MVR)	43	cm3/10min	ISO 1133
溫度(Temperature)	300	°C	ISO 1133
負載(Load)	1.2	kg	ISO 1133

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
拉伸模量(Tensile Modulus)	2600	MPa	ISO 527-1/-2
屈服應力(Yield stress)	71	MPa	ISO 527-1/-2
屈服應變(Yield strain)	5	%	ISO 527-1/-2
破壞時應變(Stress at break)	61	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	>50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	132	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	132	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	5	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	5	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	2530	MPa	ISO 178
懸臂梁式沖擊切口 (23°C)	6	kJ/m2	ISO 180/1A
懸臂梁式沖擊切口	5	kJ/m2	ISO 180/1A
溫度(Temperature)	-30	°C	ISO 180/1A
懸臂梁式沖擊無切口(Izod Impact unnotched) (23°C)	183	kJ/m2	ISO 180/1U
ASTM數據(ASTM Data)
拉伸模量(Tensile Modulus)	2700	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Yield	70	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	70	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	5	%	ASTM D 638
斷裂伸長率(Elongation at Break)	100	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	2470	MPa	ASTM D 790
懸臂梁式沖擊切口 (1/8 in)	0.0384	kJ/m	ASTM D 256
懸臂梁式沖擊切口 (Low-溫度(Temperature))	0.0432	kJ/m	ASTM D 256
溫度(Temperature)	-30	°C	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數據
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	97	°C	ISO 75-1/-2
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	111	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	72	E-6/K	ISO 11359-1/-2
COEFF線性熱(Coeff. of linear therm. expansion) (normal)	74	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	V-2	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
ASTM數據(ASTM Data)
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	66	E-6/K	ASTM D 696
熱膨脹系數(Coefficient of Thermal Expansion) (TD)	67	E-6/K	ASTM D 696
DTUL @ 264 psi	94	°C	ASTM D 648
Vicat 溫度(Temperature)	112	°C	ASTM D 1525

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsTransparentRegional Availability .

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/wuxingbiao/show-97804.html

免責聲明: 本文 Lexan ML7686|PC|沙特基礎 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡