Lexan ML3290|PC|沙特基礎物性表: Lexan ML3290|PC|沙特基礎物性表及特性介紹,Lexan ML3290|PC|沙特基礎注塑參數(shù)詳情,如需Lexan ML3290|PC|沙特基礎下載, 可到相關下載區(qū)下載

流變性能(Rheological properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
熔體體積流動速率(Melt volume-flow rate) (MVR)	8	cm3/10min	ISO 1133
溫度(Temperature)	300	°C	ISO 1133
負載(Load)	2.16	kg	ISO 1133
成型收縮(Molding shrinkage) (parallel)	0.6	%	ISO 294-4, 2577

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
拉伸模量(Tensile Modulus)	2350	MPa	ISO 527-1/-2
屈服應力(Yield stress)	60	MPa	ISO 527-1/-2
屈服應變(Yield strain)	6	%	ISO 527-1/-2
破壞時應變(Stress at break)	55	MPa	ISO 527-1/-2
破壞時應變(Strain at break)	>50	%	ISO 527-1/-2
簡支梁沖擊強度(Charpy impact strength) (+23°C)	N	kJ/m2	ISO 179/1eU
簡支梁沖擊強度(Charpy impact strength) (-30°C)	N	kJ/m2	ISO 179/1eU
簡支梁缺口沖擊強度(Charpy notched impact strength) (+23°C)	65	kJ/m2	ISO 179/1eA
簡支梁缺口沖擊強度(Charpy notched impact strength) (-30°C)	12	kJ/m2	ISO 179/1eA
彎曲彈性模量(Flexural modulus) (23°C)	2300	MPa	ISO 178
懸臂梁式?jīng)_擊切口 (23°C)	65	kJ/m2	ISO 180/1A
懸臂梁式?jīng)_擊切口	12	kJ/m2	ISO 180/1A
溫度(Temperature)	-30	°C	ISO 180/1A
懸臂梁式?jīng)_擊無切口(Izod Impact unnotched) (23°C)	N	kJ/m2	ISO 180/1U
球壓痕硬度(Ball indentation hardness)	95	MPa	ISO 2039-1

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
溫度負荷變形(Temp. of deflection under load) (1.80 MPa)	124	°C	ISO 75-1/-2
溫度負荷變形(Temp. of deflection under load) (0.45 MPa)	136	°C	ISO 75-1/-2
Vicat softening temperature A	148	°C	ISO 306
維卡軟化溫度（50℃/ h的50N）Vicat softening temperature	146	°C	ISO 306
COEFF線性熱(Coeff. of linear therm. expansion) (parallel)	70	E-6/K	ISO 11359-1/-2
Burning behav. at 1.5 mm nom. thickn.	V-2	class	IEC 60695-11-10
厚度測試(Thickness tested)	1.5	mm	IEC 60695-11-10
燃燒性厚度(Burning behav. at thickness h)	V-0	class	IEC 60695-11-10
厚度測試(Thickness tested)	2.0	mm	IEC 60695-11-10
Oxygen index	25	%	ISO 4589-1/-2

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
相對介電常數(shù)(Relative permittivity) (1MHz)	2.7	-	IEC 60250
耗散因數(shù)(耗散因數(shù)(Dissipation factor)) (1MHz)	100	E-4	IEC 60250
體積電阻率(Volume resistivity)	>1E13	Ohm*m	IEC 60093
表面電阻率(Surface resistivity)	>1E15	Ohm	IEC 60093
電氣強度(Electric strength)	35	kV/mm	IEC 60243-1
相比漏電起痕指數(shù)(Comparative tracking index)	225	-	IEC 60112

流變計算屬性(Rheological calculation properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ISO數(shù)據(jù)
熔體熱導率(Thermal conductivity of melt)	0.2	W/(m K)	-

CharacteristicsProcessingInjection Molding, Profile ExtrusionRegional AvailabilityEurope, Near East/AfricaDisclaimerCopyright M-Base .