Lexan 123|PC|沙特基礎物性表: Lexan 123|PC|沙特基礎物性表及特性介紹,Lexan 123|PC|沙特基礎注塑參數詳情,如需Lexan 123|PC|沙特基礎下載, 可到相關下載區下載

加工/物理特性	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
熔體流動指數(Melt Flow Index)	17.5	g/10min	ASTM D 1238
模具收縮(Mold Shrinkage) (MD)	0.006	mm/mm	ASTM D 955
密度(Density) (73°F)	1200	kg/m3	ASTM D 792
吸水率(Water Absorption) (24hr)	0.15	%	ASTM D 570
吸水率(Water Absorption) (Equilibrium)	0.35	%	ASTM D 570

機械性能(機械性能(Mechanical properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
抗拉強度(Tensile Strength) at Yield	61.4	MPa	ASTM D 638
抗拉強度(Tensile Strength) at Break	64.8	MPa	ASTM D 638
屈服伸長率(Elongation at Yield)	7	%	ASTM D 638
斷裂伸長率(Elongation at Break)	110	%	ASTM D 638
彎曲彈性模量(彎曲彈性模量(Flexural Modulus))	2337.32	MPa	ASTM D 790
抗彎強度(Flexural Strength)	92.4	MPa	ASTM D 790
洛氏硬度(Rockwell Hardness)	R 118	-	ASTM D 785
Taber Abrasion Resistance	10	mg/1000 cycles	ASTM D 1044
懸臂梁式沖擊切口 (1/8 in)	0.694	kJ/m	ASTM D 256

熱性能(熱性能(Thermal properties))	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
UL 94 阻燃等級(Flame rating)	HB	-	UL 94
厚度測試(Thickness tested)	0.762	mm	-
熱膨脹系數(Coefficient of Thermal Expansion) (MD)	68.4	E-6/K	ASTM D 696
Vicat 溫度(Temperature)	154	°C	ASTM D 1525
Thermal Conductivity (melt state)	0.19	W/(m K)	ASTM C 177
Specific Heat	798	J/(kg K)	ASTM C 351

電氣性能(Electrical properties)	值(Value)	單位(Unit)	測試標準(Test Standard)
ASTM數據(ASTM Data)
絕緣強度(Dielectric Strength) (Short Time)	15	kV/mm	ASTM D 149
耗散因數(Dissipation Factor) (60 Hz)	0.0009	-	ASTM D 150
耗散因數(Dissipation Factor) (1 MHz)	0.01	-	ASTM D 150
介電常數(Dielectric Constant) (60 Hz)	3.17	-	ASTM D 150
介電常數(Dielectric Constant) (1 MHz)	2.96	-	ASTM D 150
體積電阻率(Volume Resistivity)	>1E15	Ohm*cm	ASTM D 257

CharacteristicsProcessingInjection MoldingSpecial CharacteristicsU.V. stabilized or stable to weatherRegional AvailabilityNorth America, .